| Operating Limits | Units | Alumina Ceramics | Alumina Ceramics |
| Alumina Content | wt% | ≥ 99 | ≥ 95 |
| Volume Density | g /cm3 | 3.85 | 3.7 |
| Hardness (HRA) | HRA ≥ | 88 | 86 |
| Compressive Strength | MPa ≥ | 400 | 300 |
| Maximum Temperature | ℃ | 1500 | 1500 |
| Air Tight Test | Pass | Pass | |
| Thermal Shock Test | Pass | Pass | |
| Coefficient Of Heat Expansion | ×10-6/℃ | 8.2 | 7.5 |
| Dielectric Constant | εr20℃, 1MHz | 9.2 | 9 |
| Dielectric Loss | tanδ×10-4, 1MHz | 2 | 3 |
| Volume Resistivity | Ω·cm 20℃ | 1014 | 1013 |
| Puncture Strength | KV/mm , DC≥ | 20 | 20 |
| Acid-resistance | mg/cm2 ≤ | 0.7 | 7 |
| Alkali-resistant | mg/cm2 ≤ | 0.1 | 0.2 |
| Abrasion Resistance | g/cm2 ≤ | 0.1 | 0.2 |
| Compressive Strength | M Pa ≥ | 2800 | 2500 |
| Flexural Strength | M Pa ≥ | 350 | 200 |
| Elastic Modulus | G Pa | 350 | 300 |
| Poisson’s Ratio | 0.22 | 0.2 | |
| Thermal Conductivity | W/m·K( 20℃) | 25 | 20 |
Product detail pictures:
Related Product Guide:
Our corporation puts emphasis about the administration, the introduction of talented staff, plus the construction of team building, attempting hard to improve the quality and liability consciousness of team members. Our organization successfully attained IS9001 Certification and European CE Certification of Europe style for Burgmann Mg12 - Alumina Ceramic Rings – Xindeng, The product will supply to all over the world, such as: Turin, New York, Yemen, We are proud to supply our products to every costumer all around the world with our flexible, fast efficient services and strictest quality control standard which has always approved and praised by customers.
By Priscilla from Doha - 2018.11.22 12:28
Timely delivery, strict implementation of the contract provisions of the goods, encountered special circumstances, but also actively cooperate, a trustworthy company!
By Doreen from Guinea - 2018.09.29 17:23