Technical Parameters
Operating Limits | Units | Alumina Ceramics | Alumina Ceramics |
Alumina Content | wt% | ≥ 99 | ≥ 95 |
Volume Density | g /cm3 | 3.85 | 3.7 |
Hardness (HRA) | HRA ≥ | 88 | 86 |
Compressive Strength | MPa ≥ | 400 | 300 |
Maximum Temperature | ℃ | 1500 | 1500 |
Air Tight Test | Pass | Pass | |
Thermal Shock Test | Pass | Pass | |
Coefficient Of Heat Expansion | ×10-6/℃ | 8.2 | 7.5 |
Dielectric Constant | εr20℃, 1MHz | 9.2 | 9 |
Dielectric Loss | tanδ×10-4, 1MHz | 2 | 3 |
Volume Resistivity | Ω·cm 20℃ | 1014 | 1013 |
Puncture Strength | KV/mm , DC≥ | 20 | 20 |
Acid-resistance | mg/cm2 ≤ | 0.7 | 7 |
Alkali-resistant | mg/cm2 ≤ | 0.1 | 0.2 |
Abrasion Resistance | g/cm2 ≤ | 0.1 | 0.2 |
Compressive Strength | M Pa ≥ | 2800 | 2500 |
Flexural Strength | M Pa ≥ | 350 | 200 |
Elastic Modulus | G Pa | 350 | 300 |
Poisson’s Ratio | 0.22 | 0.2 | |
Thermal Conductivity | W/m·K( 20℃) | 25 | 20 |
Product detail pictures:
Related Product Guide:
We purpose to understand high quality disfigurement with the output and supply the top service to domestic and overseas buyers wholeheartedly for High reputation Single Mechanical Seal - Alumina Ceramic Rings – Xindeng, The product will supply to all over the world, such as: South Korea, United Kingdom, Algeria, There are advanced producing & processing equipment and skilled workers to ensure the merchandise with high quality. We've got found an excellent before-sale, sale, after-sale service to ensure the customers that could rest assured to make orders. Until now our merchandise are now moving on fast and very popular in South America, East Asia, the Middle east, Africa, etc.
By Meredith from Costa rica - 2018.07.27 12:26
Wide range, good quality, reasonable prices and good service, advanced equipment, excellent talents and continuously strengthened technology forces,a nice business partner.
By Miguel from Ghana - 2018.10.09 19:07